  In this paper, we report the spin glass-like coexistence of Ferromagnetic
(FM), paramagnetic (PM) and antiferromagnetic (AFM) orders in oxygen deficient
V2O5 nanoparticles (NP). It has a chemical stoichiometry of nearly V2O4.65 and
a bandgap of nearly 2.2 eV with gap states due to significant defect density.
The temperature dependent electrical conductivity and thermopower measurements
clearly demonstrate a polaronic conduction mechanism of small polaron hopping
with hopping energy of about 0.112 eV. The V2O5 sample shows a strong field as
well as temperature dependent magnetic behavior when measured using a sensitive
SQUID magnetometer. It shows a positive magnetic susceptibility over the entire
temperature range (2- 350 K). The FC-ZFC data shows clear hysteresis indicating
glassy behavior with dominant superparamagnetism (SPM). The Curie-Weiss fitting
confirms the AFM to PM transition at nearly 280 K and the curie constant yields
1.56 muB which is close to single electron moment. The small polaron formation,
which arises due to oxygen vacancy defects compensated by charge defects of
V4+, results in Magneto-Electronic Phase Separation (MEPS) and hence various
magnetic exchanges, as predicted by first principle calculations. This is
further revealed as strong hybridization of V bonded to oxygen vacancy VO and
neighboring V5+ ions, resulting in net magnetic moment per vacancy (1.77 muB
which is in good agreement with experiment). Besides, the rise in V4+ defects
is found to show AFM component as observed from the calculations. Thus, the
diversity in magnetism of undoped V2O5 has its origin in defect number density
as well as their random distribution led to MEPS. This involves localized spins
in polarons and their FM clusters on the PM background while, V4+ dimers within
and across the ladder, inducing AFM interactions.