  Recently, Heusler alloys-based spin gapless semiconductors (SGSs) with high
Curie temperature (TC) and sizeable spin polarization have emerged as potential
candidates for tunable spintronic applications. We report comprehensive
investigation of the temperature dependent ANE and intrinsic longitudinal spin
Seebeck effect (LSSE) in CoFeCrGa thin films grown on MgO substrates. Our
findings show the anomalous Nernst coefficient for the MgO/CoFeCrGa (95 nm)
film is $\cong 1.86$ micro V/K at room temperature which is nearly two orders
of magnitude higher than that of the bulk polycrystalline sample of CoFeCrGa (=
0.018 micro V/K) but comparable to that of the magnetic Weyl semimetal Co2MnGa
thin film (2-3 micro V/K). Furthermore, the LSSE coefficient for our
MgO/CoFeCrGa(95nm)/Pt(5nm) heterostructure is $\cong 20.5$ $\mu$V/K/$\Omega$ at
room temperature which is twice larger than that of the half-metallic
ferromagnetic La$_{0.7}$Sr$_{0.3}$MnO$_3$ thin films ($\cong$ 20.5
$\mu$V/K/$\Omega$). We show that both ANE and LSSE coefficients follow
identical temperature dependences and exhibit a maximum at $\cong$ 225 K which
is understood as the combined effects of inelastic magnon scatterings and
reduced magnon population at low temperatures. Our analyses not only indicate
that the extrinsic skew scattering is the dominating mechanism for ANE in these
films but also provide critical insights into the functional form of the
observed temperature dependent LSSE at low temperatures. Furthermore, by
employing radio frequency transverse susceptibility and broadband ferromagnetic
resonance in combination with the LSSE measurements, we establish a correlation
among the observed LSSE signal, magnetic anisotropy and Gilbert damping of the
CoFeCrGa thin films, which will be beneficial for fabricating tunable and
highly efficient Heusler alloys based spincaloritronic nanodevices.