  We study the magnetocaloric effect and critical behavior of
Co$_2$Cr$_{1-x}$Mn$_x$Al ($x=$ 0.25, 0.5, 0.75) Heusler alloys across the
ferromagnetic (FM) transition (T$_{\rm C}$). The Rietveld refinement of x-ray
diffraction patterns exhibit single phase cubic structure for all the samples.
The temperature dependent magnetic susceptibility $\chi$(T) data show a
systematic enhancement in the Curie temperature and effective magnetic moment
with Mn concentration, which is consistent with the Slater-Pauling behavior.
The M(H) isotherms also exhibit the FM ordering and the analysis of $\chi$(T)
data indicates the nature of the phase transition to be a second order, which
is further supported by scaling of the entropy curves and Arrott plot.
Interestingly, the Mn substitution causes an increase in the magnetic entropy
change and hence large relative cooling power for multi-stage magnetic
refrigerator applications. In order to understand the nature of the magnetic
phase transition we examine the critical exponents $\beta$, $\gamma$, $\delta$
for the $x=$ 0.75 sample by the modified Arrott plot and the critical isotherm
analysis, which is further confirmed by Kouvel-Fisher method and Widom scaling
relation, respectively. The estimated values of $\beta=$ 0.507, $\gamma=$
1.056, $\delta=$ 3.084 are found to be close to the mean field theoretical
values. The renormalized isotherms (m vs h) corresponding to these exponent
values collapse into two branches, above and below T$_{\rm C}$ that validates
our analysis. Our results suggest for the existence of long-range FM
interactions, which decays slower than power law as $J(r)\sim r^{-4.5}$ for a 3
dimensional mean field theory.