  Lyotropic chromonic liquid crystals (LCLCs) represent aqueous dispersions of
organic disk-like molecules that form cylindrical aggregates. Despite the
growing interest in these materials, their flow behavior is poorly understood.
Here, we explore the effect of shear on dynamic structures of the nematic LCLC,
formed by 14wt ${\%}$ water dispersion of disodium cromoglycate (DSCG). We
employ in-situ polarizing optical microscopy (POM) and small-angle and
wide-angle X-ray scattering (SAXS/WAXS) to obtain independent and complementary
information on the director structures over a wide range of shear rates. The
DSCG nematic shows a shear-thinning behavior with two shear-thinning regions
(Region I at $\dot{\gamma}<1\,s^{-1}$ and Region III at $\dot{\gamma}>10
s^{-1}$) separated by a pseudo-Newtonian Region II ($1 s^{-1}<\dot{\gamma}<10
s^{-1}$). The material is of a tumbling type. In Region I, $\dot{\gamma}<1
s^{-1}$, the director realigns along the vorticity axis. An increase of
$\dot{\gamma}$ above $1 s^{-1}$ triggers nucleation of disclination loops. The
disclinations introduce patches of the director that deviates from the
vorticity direction and form a polydomain texture. Extension of the domains
along the flow and along the vorticity direction decreases with the increase of
the shear rate to $10 s^{-1}$. Above $10 s^{-1}$, the domains begin to elongate
along the flow. At $\dot{\gamma}>100 s^{-1}$, the texture evolves into periodic
stripes in which the director is predominantly along the flow with left and
right tilts. The period of stripes decreases with an increase of
$\dot{\gamma}$. The shear-induced transformations are explained by the balance
of the elastic and viscous energies. In particular, nucleation of disclinations
is associated with an increase of the elastic energy at the walls separating
nonsingular domains with different director tilts.