  Magnetic and electrical properties of four series of rare earth cobaltates of
the formula La0.7-xLnxCa0.3CoO3 with Ln = Pr, Nd, Gd and Dy have been
investigated. Compositions close to x = 0.0 contain large ferromagnetic
clusters or domains, and show Brillouin-like behaviour of the field-cooled DC
magnetization data with fairly high ferromagnetic Tc values, besides low
electrical resistivities with near-zero temperature coefficients. The
zero-field-cooled data generally show a non-monotonic behaviour with a peak at
a temperatures slightly lower than Tc. The near x = 0.0 compositions show a
prominent peak corresponding to the Tc in the AC-susceptibility data. The
ferromagnetic Tc varies linearly with x or the average radius of the A-site
cations, (rA). With increase in x or decrease in (rA), the magnetization value
at any given temperature decreases markedly and the AC-susceptibility
measurements show a prominent transition arising from small magnetic clusters
with some characteristics of a spin-glass. Electrical resistivity increases
with increase in x, showed a significant increase around a critical value of x
or (rA), at which composition the small clusters also begin to dominate. These
properties can be understood in terms of a phase separation scenario wherein
large magnetic clusters give way to smaller ones with increase in x, with both
types of clusters being present in certain compositions. The changes in
magnetic and electrical properties occur parallely since the large
ferromagnetic clusters are hole-rich and the small clusters are hole-poor.
Variable-range hopping seems to occur at low temperatures in these cobaltates.