  This work presents a theoretical study regarding photovoltaic (PV) &
thermoelectric (TE) applications of ScAgC. The electronic, optical and
thermoelectric properties are investigated using DFT and semi-classical
Boltzmann transport theory. DFT calculates a direct band-gap of $\sim$$0.47$
eV, while $G_{0}W_{0}$ method estimates a band-gap of $\sim1.01$ eV. We used
parabola fitting to estimate effective mass ($m^{*}$) values for bands B1-B4 at
$\Gamma$-point, which are $\sim$ -0.087 (-0.075), $\sim$ -0.17 (-0.27), $\sim$
-0.17 (-0.27), and $\sim$ 0.049 (0.058) along the $\Gamma-X$ ($\Gamma-L$)
direction, respectively. We also examine phonon dispersion and thermal
properties. Furthermore, optoelectronics' properties are calculated within the
energy range of 0 to 10 eV. The optical conductivity $\sigma (\omega)$,
refractive index $\tilde{n}(\omega)$, and dielectric function $\epsilon
(\omega)$ show strong optical transitions in the visible region. The lowest
calculated value of reflectivity r($\omega$) is $\sim$0.24 at $\sim$4.7 eV, and
the highest calculated value of absorption coefficient $\alpha (\omega )$ is
$\sim1.7\times 10^{6} cm^{-1}$ at $\sim$ 8.5 eV. At 300 K, we expect a maximum
solar efficiency (SLME) of $\sim$33% at $\sim$1 $\mu m$. The lattice thermal
conductivity $\kappa_{ph}$ shows maximum value of $\sim$3.8 W$m^{-1}K^{-1}$ at
1200 K. At 1200 K, for electron doping of $\sim$3.9$\times$$10^{21}$$cm^{-3}$,
the maximum value of $S^{2}\sigma /\tau$ is $\sim$145 $\times 10^{14}$ $\mu
WK^{-2}cm^{-1}s^{-1}$, while for hole doping of
$\sim$1.5$\times$$10^{21}$$cm^{-3}$, it is $\sim$123 $\times 10^{14}$ $\mu
WK^{-2}cm^{-1}s^{-1}$. The highest $ZT$ at 1200 K is expected to be $\sim$0.53,
whereas the optimal \%efficiency is predicted as $\sim$8.5% for cold (hot)
temperatures of 300 (1200) K. The results suggest that ScAgC can be a potential
candidate for solar cell and TE applications.